Posts posted by Loulougirl

  1. Good tip Barbra, thanks! :)

    Well, I tried it last night ... I think perhaps I cooked it, left it in the crockpot, a tad too long. It was rather lumpy and thick when I gloped it into the mold. Course.. this is my first time, maybe that's just the way it is! lol

    I tried a tiny piece that crumbled off when I cut it this morning.. so nice!

    I really liked how this worked, so I think this will be go to option for fo's that overheat or trace fast! :)

  2. I was just getting things ready to try it tonight, when I thought of something. I normally discount my water when doing CP. Should I use full water to HP? I read on a few sites that it's better to use the full water amt.

    What do you ladies think?

  3. Hi all :)

    I'm planning on trying hot process this weekend. I've been reading up on all the old threads about it, found some tutorials.. I'm pretty excited! :)

    I was just wondering if anyone had any tips for HP :) I appreciate it!

  4. I use both, VS and the Browning Neutralizer in different products. If I use it, everything stays as it should. If not, I get brown spots within hours on bath bombs or bubble bars. Some Pink Sugar body butter I made my Mom is just now turning light tan, about 3 months later.

    Funny thing... I was in Lush yesterday, and I noticed brown spots on some of their bath bombs! :shocked2:

  5. Oh wow that's SO pretty!!

    So leaving it a bit longer in the mold will keep the sides nicer? I have a silicone liner for my wood mold, and I noticed the last few batches looked rough on all the outside edges. Next time I'll leave it longer and see what happens!

×
×