  1. I could certainly understand using the complete 18% with a light scent. I've personally used right now with my Gw464 and Ecosoy @ 12%. With the Ecosoy im still barely getting a HT at 12% but alot more than what i was getting @ 6-9%. However with the Gw464 im using at 12% with a stronger scent and the HT and CT has improved significantly. Currently ive pushed myself back to the testing stage with wicks/fo load combo's. with the new Ecosoy coming out i am excited to push it a little bit further than just 12% maybe a 14 or even 15. 2oz (12%) with a Premier Sm and or Premier Md. Here in Canada, very limited on wicks to use and have found that premiers are almost perfect "almost". Any suggestions on wicks that would improve even more the HT with the GW464? Thanks for your input @Jcandleattic
  2. Hey Everyone i managed to find some new information on the new EcoSoy coming out! Can't wait for testing! Thoughts?
  3. Thanks for the response, maybe im not recognizing it as frosting, as im still a bit newbish. But, i only really have this issue with the molds and not my glass candles, maybe im doing something wrong with the PillarBlend. Would dropping it in pour temperature change/help cut down on this? i know i can't go to low, as i like Shiny candles, and dont want a mottled candle. Being in Canada, during the winter months for pouring candles can really be an issue lol. Would having the mold warmed before pour help?
  4. Yes i do got a heat gun, i had tried using the heat gun/paper towel method but was still left with spots/ very tiny almost pitted like, and sometime a rough patch but then the rest of the candle top would turn out smooth and shiny. its very odd, maybe im doing something wrong, or haven't done something correctly. they are a metal mold (tin plated steel) and purchased from a local candle shop, https://villagecraftandcandle.com/candle-making/accessories/metal-candle-molds/scallop-flower-mold might be just the mold maybe? im not sure, the candle i did last night after a good wiping and heating turned out significantly better than some of my other ones but still a few spots and not perfect. maybe im just being too picky lol. ive included a couple pictures too maybe help in determining what the problem maybe.
  5. American Soy Organics P100 Ultimate Pillar Blend and Ecosoy PB they both leave kind of a residue in the bottom, and then even after being wiped out it still leaves marks on the top of my candles. Is it possible due to a temperature issue? Maybe use a little more heat on my mold before pour, especially the bottom (top)? Or should i go 5-10 degrees hotter or cooler? Both waxes i melt at 180-185 and pour at 170
  6. Thank You! The issue im getting, even when poured correctly those spots are appearing on my candle and its just nasty looking, but maybe im not tempering them enough before use? I'm not sure but will play around with it. Again, Thank You!
  7. Hi there, i've read on several posts people either use the oven method and or a solution-based cleaning agent. I dont have wax buildup on the inside of my molds its more of like residue from the wax, and i am wondering the best way to get the molds "spotless" again. Would it be just as easy to use my heat gun and wipe or more of solution-type spray and wipe? any help would be great. Thanks
  8. Hello All, Newbie to the forum, looking for some help on this specific type of wax P100 Ultimate Pillar Blend (American Soy Organics). The issue i'm having is to do with the pour temperature, climate changes here in Canada, and where i do my candles, i cannot control my heat. Does anyone here have any experience in using this wax? Currently, i pour at about 175F - 180F to eliminate snowflaking on the top, biggest issue i have due to heat is it dips starts high then goes inward to the wick. I can help with most of this issue with the use of my heat gun, with only doing one-pour. With this wax, with the FO% does anyone use a high % like 12% currently im sitting at about 9% and still barely a HT with it. Current wick that i find works best is the Premier Cotton using the smalls testing out the mediums today. any help would be appreciated. Thanks and Happy Candle making.
×
×